Material Data Sheet

• Proprietary SM25CR series. TGP 3706 (latest revision)
• API 5CT / ISO11960
• NACE MR0175 / ISO 15156
• API RP 5C1 / ISO 10405
• API 5CRA  / ISO 13680  
• VAM Book
• Nippon Steel Storage and handling procedure for CRA materials

Corrosive production environments featuring combined presence of CO₂ + low H₂S + Chlorides.

 Its primary function is Tubing and Liner, sections permanently exposed to production fluids

In production environments, SM25CR is typically fit for deep, HP-HT applications requiring high strength materials where localized corrosion is a concern (high temperature, high chlorides and low pH).

Final material application in production environments will be driven by CO₂, H₂S, Temperature, pH and expected Chlorides content.

In addition, compatibility with packer & completion fluids (brines and additives), matrix acidizing fluids, and scale dissolvers need to be ascertained.

For a more detailed assessment please contact Nippon Steel engineers. 

(mass %)

UNS Number: S31260

* Data will be shortly available.

In wet CO₂ environments, one of the main limitations of Martensitic Stainless Steels (either as API L80-13CR or any enhanced version like SM13CRS) are:

• Corrosion Resistance in High Temperature environments
• SSC (Sulfide Stress Cracking) resistance in presence of H₂S
• SCC (Stress Corrosion Cracking) resistance in combined presence of H₂S and Chlorides.

In low content H₂S environments, Duplex materials exceed martensitic stainless steel corrosion resistance (specifically localized corrosion) following the chemistry logic where increase of elements such as Cr, Mo and W provides a more stable spontaneous passive film developed by the material when exposed to a corrosive environment.

SM25CR is recognized by ISO-13680 as Group 2 Category 25-7-3.

NACE MR0175/ISO15156’s stance concerning Duplex materials is as follows:

- For duplex material with 30<PREN <40 & containing > 1.5% Mo.

Maximum applicable H₂S is 0.3 psi (2 kPa) with any combinations of temperature, pH (in producing environment) & chlorides.

Nippon Steel’s position toward SM25CR SCC resistance is more comprehensive, where the material capability to withstand higher H₂S partial pressure will be inversely proportional to the expected Chlorides content (See Fig 1).

Fig 1: Duplex & Super Duplex Chlorides and H₂S limitation
Open: No SCC, Solid: SCC

It is worth noting that the SSC susceptibility of duplex materials is the highest between 80 to 100°C. This, in contrary to C-steel, low alloy materials or martensitic type of steel where SSC is a low/ambient temperature problem which explains why 80°C was selected to conduct SSRT test as illustrated in Figure 1.

SM25CR will feature a better resistance to SSC than SM22CR when compared at equivalent strength and applied stress levels.

Another advantage of SM25CR versus SM22CR material is its higher pitting resistance in high temperature environments as shown in Figure 2.

Fig 2: Influence of H₂S partial pressure and temperature
of pitting behavior of Duplex stainless steels

For additional information about material performances please contact Nippon Steel engineers.

A selection of critical applications of Sumitomo SM25CR is shown below. These Field records include SM25CR material used as Tubing and Liner.

While state-of-the-art HSE rules are applied throughout Nippon Steel manufacturing process, proprietary and specific HSE regulations shall be applied along the life cycle of the pipe until it reaches its final position in the well, according to each operator’s rules. This particularly applies to all phases of handling and transportation, assembly on the rig floor, and rig return if applicable. OCTG are heavy and by nature unstable. Special care shall be paid to potential risks of injury whenever handling OCTGs. Walking on pipes shall be avoided at all times. Usage of Personal Protection Equipments (PPE) is mandatory. Equipment and procedures will be established to capture the possible wastes generated during maintenance (cleaning, coating, doping) and disposed according to local regulations. This applies in particular to storage dope, running dope, or cleaning water wastes.

Best practices for transportation, handling and storage of OCTG in general are covered by ISO 10405 / API RP5C1. VAM Book is also a good source of handling practices for VAM connections. In addition to these general rules, specific care is recommended pertaining to SM25CR, because improper handling could affect the material performances and by extension the corrosion resistance :

• Prevention of Spot Hardening
• Prevention of Iron contamination
• Adapted running equipments and practices
• Prevention of corrosion on rig returns, particularly in presence of completion fluids

For more specific information please refer to Nippon Steel Storage and handling procedure for CRA materials or contact Nippon Steel engineers.